Multi-layered object comprising hard coat layer and light transmitting layer, and method for producing the same

ABSTRACT

The present invention provides a multi-layered object having a hard coat layer capable of improving anti-staining property, anti-staining durability, scratch resistance, abrasion resistance and the like. A multi-layered object comprising a hard coat layer and a light transmitting layer, wherein the hard coat layer is formed from a composition for hard coat comprising: an active energy ray-curable silicone-acrylic copolymer (A); and an active energy ray-curable polyfunctional compound (B), and wherein the active energy ray-curable silicone-acrylic copolymer (A) contains: a polysiloxane block (a-1), an acrylic block (a-2) containing an active energy ray-curable double bond group and a fluoroalkyl group-containing acrylic block (a-3).

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a multi-layered object having a hard coat layer, and a method for producing the multi-layered object. More specifically, the present invention relates to various multi-layered objects required to have anti-staining property, anti-staining durability, scratch resistance, abrasion resistance and the like, and having a hard coat layer which has these various properties on the surface thereof; and relates to a method for producing the multi-layered objects.

In particular, the present invention relates to a method for forming a hard coat layer having anti-staining property, anti-staining durability, scratch resistance, and abrasion resistance, on the surface of each of the following, without deteriorating the optical property and the recording properties: information recording media; optical lenses; optical filters; anti-reflective films; various display elements such as liquid crystal displays, CRT displays, plasma displays and EL displays; and the like, and relates to an article having the hard coat layer formed thereon.

2. Disclosure of the Related Art

Usually protective layers (hard coat layers) are provided on the surfaces of the following various articles required to have scratch resistance and abrasion resistance: information recording media such as CD (Compact Disc) and DVD (Digital Versatile Disc); optical lenses; optical filters; anti-reflective films; and various display elements such as liquid crystal displays, CRT displays, plasma displays and EL displays.

In these various articles, in the course of the use by users, the surface thereof frequently undergoes stain adhesion due to fingerprint, sebum, sweat and cosmetics. Once adhesion of such stains occurs, such stains can hardly be removed; in particular, in information recording media and optical lenses used for the recording and reproduction thereof, such stains result in significant failure in recording and reproduction of information signals to cause a serious problem.

In particular, information recording media such as BD (Blu-ray Disc) said to be next-generation DVD are undergoing adoption of shorter wavelength of recording/reproduction laser light, and high-density recording with objective lenses having high numerical apertures; along with such development, the light transmitting substrate (light transmitting layer) comes to be thinner and accordingly there occurs a possibility that minute scratches, stains and the like on the light incident-side surface cause crucial failure in recording/reproduction in a more severe manner than in conventional information recording media. From these reasons, it is strongly demanded to provide, on the light incident-side surface of the information recording media, a hard coat layer having anti-staining property, anti-staining durability, scratch resistance and abrasion resistance, without deteriorating the recording/reproduction properties.

As a method of improving the anti-staining property of a hard coat layer, there has been proposed a method of improving the anti-staining property (water repellency and oil repellency) of the surface of an information recording medium by applying silicone oil or a fluoropolymer to the surface of the hard coat layer. However, in this method, the hard coat layer is formed by applying an anti-staining agent onto the surface of the information recording medium, and hence this method offers a drawback that the anti-staining agent is dissipated in the course of the use by a user and consequently the effect of the anti-staining property is hardly maintained, that is, the hard coat layer is poor in anti-staining durability.

On the other hand, there is a method of improving the anti-staining property by incorporating an additive such as silicone oil or a fluoropolymer into the hard coat layer. However, these additives are the substances generally referred to as soft segment and have a property to impart flexibility to a resin, and hence the addition of these additives offers a drawback to degrade the mechanical strength of the hard coat layer such as the surface hardness as a function of the hard coat layer.

For example, Japanese Patent Laid-Open No. 2004-047040 (Patent Document 1) describes an optical recording medium characterized in that a coating layer made of an anti-staining agent is formed on the reading side surface on which incident is the laser light conducting at least recording or reproduction of the information signal (claim 1). However, the anti-staining agent described in Patent Document 1 includes an alkoxysilane compound having a perfluoro polyether group or a fluoroalkyl group, and is different from the composition for the hard coat layer according to the present invention.

Japanese Patent Laid-Open No. 2002-367229 (Patent Document 2) describes an optical information recording medium in which at least a reflective film, a recording film and a protective film are provided on one surface of the substrate of the optical information recording medium, and the protective film is formed as a surface layer on the one surface of the substrate, wherein a hard coat resin layer is formed as an outer layer of at least one selected from the substrate and the protective film, and a chemical adsorption film made of organic silane molecules is formed as an outer layer of the hard coat resin layer so as to be bonded to the hard coat layer through a covalent bond (claim 1). The hard coat layer of Patent Document 2 is, as described therein, a so-called double layered hard coat layer in which the chemical adsorption film formed by covalent bonds is further provided on the surface of the hard coat resin layer, and is significantly different in constitution from the hard coat layer of the present invention.

Japanese Patent Laid-Open No. 2006-107572 (Patent Document 3) describes a hard coat surface treatment method wherein a hard coat surface formed by curing an organic hard coat material containing an energy ray curable compound is subjected to a plasma treatment in an atmosphere into which introduced is a gas of a fluorinated hydrocarbon containing fluorine atoms in the molecule (claim 1). Patent Document 3 describes that according to this method, there is provided a hard coat surface treatment method in which the medium surface is imparted with water repellency and oil repellency by means of a low cost and simple process; however, this method requires a specific large scale apparatus in order to conduct the plasma treatment under a specific atmosphere, and hence is insufficient as a simple and low cost process.

Japanese Patent Laid-Open No. 2003-277478 (Patent Document 4) describes an epoxy resin composition that includes: an epoxy resin having in one molecule at least two cyclic aliphatic epoxy groups, at least one perfluoroalkyl group having 6 to 12 carbon atoms and at least one alkylsiloxane group; and a cationic polymerization catalyst, wherein the cyclic aliphatic epoxy group and the perfluoroalkyl group are present in the branched chains of the epoxy resin, and the alkylsiloxane group is present in the main chain of the epoxy resin (claim 1). Patent Document 4 is concerned with a composition that is applied to a liquid jet recording head, and the layer formed from the composition has anti-staining property, but is insufficient for a hard coat layer that also has the mechanical strength such as the surface hardness required in information recording media, various display elements or the like.

Japanese Patent Laid-Open No. 2005-206829 (Patent Document 5) describes a fluorine-containing curable coating liquid containing a fluorine-containing compound having a film formability and a polymerizable double bond, and a fluorine-containing (meth)acrylic acid ester having no film formability (claim 1). Similarly to Patent Document 4, the layer formed from the coating liquid of Patent Document 5 has anti-staining property, but is insufficient for a hard coat layer that also has the mechanical strength such as the surface hardness required in information recording media, various display elements or the like. As a technique to improve the surface hardness, it is possible to provide a hard coat layer and to form thereon a fluorine-containing curable coating film; however, this method suffers from a trouble that the fluorine-containing curable coating film is dissipated in the course of the use by a user to lead to poor anti-staining durability.

Japanese Patent Laid-Open No. 11-43648 (Patent Document 6) describes a curable resin composition for a coating material including: (a) a silicone-acrylic block copolymer obtained by polymerizing at least one kind of acrylic monomer having a cross-linkable functional group or a mixture composed of said acrylic monomer and another ethylenically unsaturated monomer in the presence of a silicone macro initiator that includes a plurality of polysiloxane chains having both terminals linked with a 2,2′-azobisnitrile group; (b) a film forming resin having a functional group capable of cross-linking with the same curing agent as for the cross-linkable functional group of the (a) component, or having a functional group that mutually reacts with the functional group of the (a) component; and (c) a curing agent that reacts at least with the (b) component (claim 1). However, the composition described in Patent Document 6 is different from the composition applied to the present invention, and is insufficient for the hard coat layer having anti-staining property, anti-staining durability, scratch resistance and abrasion resistance, without impairing the optical properties and the recording properties as required for information recording media and various display elements.

Japanese Patent Laid-Open No. 2002-363495 (Patent Document 7) describes a coating composition including: (a) a fluorine/silicone-acrylic block copolymer obtained by polymerizing a monomer mixture A including a fluorine-containing unsaturated monomer (a-1) and an acrylic monomer (a-2) having a reactive functional group, in the presence of a silicone macro initiator that includes a plurality of polysiloxane chains having both terminals linked with a 2,2′-azobisnitrile group; (b) a fluorine-containing copolymer obtained by polymerizing a monomer mixture B including a fluorine-containing unsaturated monomer (b-1) and an acrylic monomer (b-2) having a reactive functional group; and (c) a curing agent (claim 1). However, the composition described in Patent Document 7 is different from the composition applied to the present invention, and is insufficient for the hard coat layer having anti-staining property, anti-staining durability, scratch resistance and abrasion resistance, without impairing the optical properties and the recording properties as required for information recording media and various display elements.

SUMMARY OF THE INVENTION

An object of the present invention is to inexpensively provide a multi-layered object having a hard coat layer formed thereon excellent in anti-staining property, anti-staining durability, scratch resistance and abrasion resistance, by solving the above-described conventional technical problems. Additionally, another object of the present invention is to provide a production method for forming inexpensively and easily a multi-layered object having a hard coat layer excellent in anti-staining property, anti-staining durability, scratch resistance and abrasion resistance.

The present invention provides a multi-layered object comprising a hard coat layer and a light transmitting layer to thereby achieve the above-described objects of the present invention,

wherein the hard coat layer is formed from a composition for hard coat comprising: an active energy ray-curable silicone-acrylic copolymer (A); and an active energy ray-curable polyfunctional compound (B), and

wherein the active energy ray-curable silicone-acrylic copolymer (A) contains:

a polysiloxane block (a-1) represented by the following formula (I):

wherein R¹s and R²s are the same or different and each represents a hydrogen atom, an alkyl group having 1 to 6 carbon atoms or a nitrile group; R³s are the same or different and each represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms; R⁴s are the same or different and each represents a hydrogen atom, a halogen atom, a substituted or nonsubstituted alkyl group having 1 to 6 carbon atoms or a phenyl group having 6 to 12 carbon atoms; p and q are the same or different and each represents an integer of 0 to 6; and m represents an integer of 0 to 600,

an acrylic block (a-2) containing an active energy ray-curable double bond group, and

a fluoroalkyl group-containing acrylic block (a-3).

The above-described composition for hard coat further may comprise a photopolymerization initiator (C), if necessary.

The above-described composition for hard coat further may comprise an inorganic filler (D), if necessary.

The weight ratios of the individual blocks constituting the above-described active energy ray-curable silicone-acrylic copolymer (A) are preferably as follows:

the polysiloxane block (a-1): 0.1 to 40% by weight;

the acrylic block (a-2) containing the active energy ray-curable double bond group: 5 to 94.8% by weight; and

the fluoroalkyl group-containing acrylic block (a-3): 4.9 to 49.9% by weight.

The above-described light transmitting layer is preferably formed from an active energy ray-curable material including a urethane (meth)acrylate oligomer.

The present invention also provides an information recording medium comprising the above-described multi-layered object.

The present invention also provides a method for producing a multi-layered object comprising a hard coat layer and a light transmitting layer, the method comprising the step of:

applying a composition for hard coat onto a light transmitting layer to form a hard coat layer,

wherein the composition for hard coat comprises:

an active energy ray-curable silicone-acrylic copolymer (A); and

an active energy ray-curable polyfunctional compound (B),

wherein the active energy ray-curable silicone-acrylic copolymer (A) contains:

a polysiloxane block (a-1) represented by the following formula (I):

wherein R¹s and R²s are the same or different and each represents a hydrogen atom, an alkyl group having 1 to 6 carbon atoms or a nitrile group; R³s are the same or different and each represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms; R⁴s are the same or different and each represents a hydrogen atom, a halogen atom, a substituted or nonsubstituted alkyl group having 1 to 6 carbon atoms or a phenyl group having 6 to 12 carbon atoms; p and q are the same or different and each represents an integer of 0 to 6; and m represents an integer of 0 to 600,

an acrylic block (a-2) containing an active energy ray-curable double bond group, and

a fluoroalkyl group-containing acrylic block (a-3).

In the above-described method for producing the multi-layered object, it is preferable to form the hard coat layer by applying the composition for hard coat under the condition that the light transmitting layer is still uncured or half cured.

The multi-layered object of the present invention has a single-layered hard coat layer, and hence is provided with anti-staining property, scratch resistance and abrasion resistance, without deteriorating the optical properties and recording properties as required for information recording media and various display elements, and further is excellent in the anti-staining durability enabling a long-term maintenance of the anti-staining property.

Additionally, the hard coat layer included in the multi-layered object of the present invention is active energy-ray curable, and hence is excellent in the production efficiency and the production cost. Thus, the present invention enables more inexpensive, simpler and easier provision of a multi-layered object having a hard coat layer having anti-staining property, anti-staining durability, scratch resistance and abrasion resistance.

In particular, formation of the hard coat layer on the surface of the light transmitting layer in an information recording medium enables to conduct recording/reproduction on an information recording medium without deteriorating the optical properties and recording properties required for information recording media, and additionally enables to obtain an information recording medium excellent in anti-staining property, anti-staining durability, scratch resistance, and abrasion resistance.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic cross-sectional view illustrating an example of the layer structure of an information recording medium comprising a multi-layered object of the present invention;

FIG. 2 is a schematic cross-sectional view illustrating an example of the layer structure of an information recording medium comprising a multi-layered object of the present invention;

FIG. 3 is a schematic cross-sectional view illustrating another example of the layer structure of an information recording medium comprising a multi-layered object of the present invention; and

FIG. 4 is a schematic cross-sectional view illustrating another example of the layer structure of an information recording medium comprising a multi-layered object of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

A hard coat layer included in a multi-layered object of the present invention is obtained from a composition for hard coat comprising: an active energy ray-curable silicone-acrylic copolymer (A); and an active energy ray-curable polyfunctional compound (B); and optionally a photopolymerization initiator (C); and optionally an inorganic filler (D). Hereinafter, the individual components are described in detail.

Active Energy Ray-Curable Silicone-Acrylic Copolymer (A)

The active energy ray-curable silicone-acrylic copolymer (A) contains at least the following blocks:

a polysiloxane block (a-1),

an acrylic block (a-2) containing an active energy ray-curable double bond group, and

a fluoroalkyl group-containing acrylic block (a-3). By forming the hard coat layer included in the multi-layered object of the present invention from a composition for hard coat including the active energy ray-curable silicone-acrylic copolymer, a hard coat layer excellent in anti-staining property, anti-staining durability, scratch resistance, abrasion resistance and the like is obtained.

Polysiloxane Block (a-1)

Examples of the polysiloxane block (a-1) contained in the active energy ray-curable silicone-acrylic copolymer (A) in the present invention include the block represented by the following formula (I):

In the above-presented formula (I), R¹s and R²s are the same or different and each represents a hydrogen atom, an alkyl group having 1 to 6 carbon atoms or a nitrile group; R³s are the same or different and each represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms; R⁴s are the same or different and each represents a hydrogen atom, a halogen atom, a substituted or nonsubstituted alkyl group having 1 to 6 carbon atoms or a phenyl group having 6 to 12 carbon atoms; p and q are the same or different and each represents an integer of 0 to 6; and m represents an integer of 0 to 600.

More preferably, R¹s each represent a hydrogen atom or an alkyl group having 1 to 3 carbon atoms; R²s each represent a nitrile group; R³s are the same or different, and each represents a hydrogen atom or an alkyl group having 1 to 3 carbon atoms; R⁴s are the same or different and each represents a hydrogen atom, a halogen atom, a substituted or nonsubstituted alkyl group having 1 to 3 carbon atoms or a phenyl group having 6 to 9 carbon atoms; p and q are the same or different and each represents an integer of 0 to 6; and m represents an integer of 30 to 200. Particularly preferably, R¹s, R³s and R⁴s each represent a methyl group.

The inclusion of the polysiloxane block (a-1) in the active energy ray-curable silicone-acrylic copolymer (A) included in the composition for hard coat enables to improve the water repellency of the obtained hard coat layer. And, this way enables to enhance the anti-staining property of the hard coat layer. Further, this copolymer has the polysiloxane structure as the skeleton thereof, thereby the water repellency of the hard coat layer can be maintained over a long term.

Acrylic Block (a-2) Containing Active Energy Ray-Curable Double Bond Group

The active energy ray-curable double bond group-containing acrylic block (a-2) contained in the active energy ray-curable silicone-acrylic block copolymer (A) in the present invention is prepared by the copolymerization of (meth)acrylic monomers having various substituents. And, the active energy ray-curable double bond group-containing acrylic block (a-2) in the present invention is characterized by having a pendant group having an active energy ray-curable double bond group.

Examples of the active energy ray-curable double bond group included in the active energy ray-curable double bond group-containing acrylic block (a-2) include an acrylic group and a methacrylic group. Examples of the pendant group contained in the active energy ray-curable double bond group-containing acrylic block (a-2) include the group represented by the following formula (II):

In the above-presented formula (II), R⁵ represents an optionally substituted straight chain or branched alkylene group having 1 to 10 carbon atoms, and R⁶ represents a hydrogen atom or a methyl group. Examples of the substituent optionally contained in R⁵ include a hydroxy group, an alkoxy group (for example, a methoxy group, an ethoxy group, an isopropoxy group and a butoxy group), a cyano group, a halogen atom (for example, Cl, Br, I and F), a carboxylic acid ester group, a sulfonic acid ester group, a nitro group and an amino group.

More preferably, R⁵ represents an optionally substituted straight chain or branched alkylene group having 1 to 6 carbon atoms, and R⁶ represents a methyl group. Examples of the substituent optionally contained in R⁵ preferably include a hydroxy group.

By including the active energy ray-curable double bond group-containing acrylic block (a-2) in the active energy ray-curable silicone-acrylic copolymer included in the composition for hard coat, the copolymer comes to acquire the active energy ray curing characteristics. The presence of the active energy ray-curable double bond group contained in the acrylic block enables to provide a copolymer that imparts a satisfactory mechanical strength to the hard coat layer. In general, examples of the active energy ray-curable group include, in addition to the active energy ray-curable double bond group, epoxy groups. These active energy ray-curable epoxy groups are generally cationically polymerizable. When the active energy ray-curable silicone-acrylic copolymer including these epoxy groups is used, it is necessary to use a cationic polymerization initiator. However, the cationic polymerization initiator is unpreferable because the residual presence of the initiator in articles may adversely affect the environment. Additionally, the use of the active energy ray-curable silicone-acrylic copolymer including epoxy groups is unpreferable because such a copolymer requires a heat curing treatment to degrade the productivity.

Fluoroalkyl Group-Containing Acrylic Block (a-3)

The active energy ray-curable silicone-acrylic copolymer (A) in the present invention contains the fluoroalkyl group-containing acrylic block (a-3). Examples of the pendant group contained in the fluoroalkyl group-containing acrylic block (a-3) include the group represented by the following formula (III):

In the above-presented formula (III), R⁷ represents an alkylene group having 1 to 6 carbon atoms; and Rf represents a straight chain or branched fluoroalkyl group having 1 to 12 carbon atoms.

More preferably, R⁷ represents an alkylene group having 1 to 3 carbon atoms, and Rf represents a straight chain fluoroalkyl group having 1 to 12 carbon atoms. Examples of the fluoroalkyl group include preferably —(CF₂)²⁻⁶H or —C_(n)F_(2n+1) (n is an integer of 1 to 12), and more preferably include —(CF₂)_(n)—CF₃ (n is an integer of 1 to 7).

The inclusion of the fluoroalkyl group-containing acrylic block (a-3) in the active energy ray-curable silicone-acrylic copolymer (A) included in the composition for hard coat enables to improve the water repellency and the oil repellency of the obtained hard coat layer. And, this way enables to enhance the anti-staining property of the obtained hard coat layer. Further, the fluoroalkyl structure possessed by this copolymer as the skeleton thereof enables the water repellency and the oil repellency of the hard coat layer to be maintained over a long term. The use of such an active energy ray-curable silicone-acrylic copolymer (A) enables to form a hard coat layer having an excellent water repellency and an excellent oil repellency, without adding any so-called fluororesin or the like.

Other Acrylic Blocks (a-4)

The active energy ray-curable silicone-acrylic copolymer (A) in the present invention may further contain other acrylic blocks (a-4) other than (a-1) to (a-3). Examples of the pendant group contained in the other acrylic block (a-4) include an alicyclic hydrocarbon group. The inclusion of such other acrylic block (a-4) in the active energy ray-curable silicone-acrylic copolymer (A) included in the composition for hard coat enables to prepare the active energy ray-curable silicone-acrylic copolymer (A) capable of imparting to the hard coat layer a satisfactory adhesion to the substrate.

The weight ratios of the individual blocks, in the present invention, constituting the active energy ray-curable silicone-acrylic copolymer (A) are preferably as follows:

the polysiloxane block (a-1): 0.1 to 40% by weight and more preferably 10 to 40% by weight;

the acrylic block (a-2) containing the active energy ray-curable double bond group: 5 to 94.8% by weight and more preferably 15 to 70% by weight; and

the fluoroalkyl group-containing acrylic block (a-3): 4.9 to 49.9% by weight and more preferably 5 to 35% by weight. When the active energy ray-curable silicone-acrylic copolymer (A) further contains the other acrylic block (a-4), the weight ratio of the other acrylic block (a-4) is 0.1 to 5% by weight and more preferably 0.1 to 3% by weight, with the proviso that the total sum of the weight ratios of the blocks (a-1), (a-2), (a-3) and (a-4) is 100% by weight.

When the weight ratio of the polysiloxane block (a-1) is less than 0.1% by weight, the polymerization reaction for producing the active energy ray-curable silicone-acrylic copolymer becomes difficult, and when exceeds 40% by weight, the flexibility of the active energy ray-curable silicone-acrylic copolymer is increased, and the weight ratio of the active energy ray-curable double bond group-containing acrylic block is decreased and consequently the hard coat property is degraded, or the weight ratio of the fluoroalkyl group-containing acrylic block is decreased to cause a possibility that no sufficient oil repellency is maintained. When the weight ratio of the active energy ray-curable double bond group-containing acrylic block (a-2) is less than 5% by weight, the active energy ray curing characteristics is insufficient to cause a possibility that the hard coat property is degraded, and when exceeds 94.8% by weight, the weight ratio of the fluoroalkyl group-containing acrylic block is decreased to cause a possibility that no sufficient oil repellency is maintained. When the weight ratio of the fluoroalkyl group-containing acrylic block (a-3) is less than 4.9% by weight, there is caused a possibility that no sufficient oil repellency is maintained, and when exceeds 49.9% by weight, the flexibility of the active energy ray-curable silicone-acrylic copolymer is increased and the weight ratio of the active energy ray-curable double bond group-containing acrylic block is decreased to cause a possibility that the hard coat property is degraded.

Preparation of the Active Energy Ray-Curable Silicone-Acrylic Copolymer (A)

As an example of the preparation method of the active energy ray-curable silicone-acrylic copolymer (A), quoted is a method in which an azo group-containing polysiloxane compound, a fluoroalkyl group-containing unsaturated monomer, and acrylic acid and/or methacrylic acid are copolymerized, and then an epoxy group-containing ethylenically unsaturated monomer is reacted. At the time of the copolymerization, other radical polymerizable monomers may also be used in combination. As another example of the preparation method of the active energy ray-curable silicone-acrylic copolymer (A), quoted is a method in which an azo group-containing polysiloxane compound, a fluoroalkyl group-containing unsaturated monomer and an epoxy group-containing ethylenically unsaturated monomer are copolymerized, and then acrylic acid and/or methacrylic acid is reacted. Also in this method, at the time of the copolymerization, other radical polymerizable monomers may be used in combination.

In these preparation methods, the monomer components other than the azo group-containing polysiloxane compound form the acrylic blocks in the active energy ray-curable silicone-acrylic copolymer (A), and the active energy ray-curable double bond group-containing acrylic block (a-2), the fluoroalkyl group-containing acrylic block (a-3), and where necessary, the other acrylic block (a-4) are formed. The use of the other radical polymerizable monomers enables to control the physical properties such as the adhesion of the hard coat layer obtained from the composition for hard coat.

Examples of the azo group-containing polysiloxane compound used for the preparation of the active energy ray-curable silicone-acrylic copolymer include the compound represented by the following formula (IV):

In the above-presented formula (IV), R¹ to R⁴, m, p and q are defined in the same manner as described above, Xs are the same or different and each represents a halogen atom, and r is an integer of 1 to 20.

The azo group-containing polysiloxane compound has a characteristic that this compound is decomposed by heating or active energy ray irradiation to generate nitrogen and radical species. The radical species generated are easily polymerized with various vinyl monomers. Accordingly, by heating or active energy ray irradiation in the presence of the azo group-containing polysiloxane compound and various vinyl monomers, the azo group-containing polysiloxane compound functions as a polymerization initiator and at the same time supplies radical species having the polysiloxane block, and consequently, the copolymer including the polysiloxane block can be easily prepared.

The azo group-containing polysiloxane compound can be prepared by acid chloridizing, for example, a 2,2′-azobisnitrile derivative having a carboxyl group such as 4,4′-azobis(4-cyanovaleric acid) and the homolog thereof, and by reacting this acid chloridized derivative with a polysiloxane chain-containing compound such as a polydimethylsiloxane having amino groups or hydroxyl groups at the both terminals thereof. Such an azo group-containing polysiloxane compound is described in Japanese Patent Publication No. 2-33053 and Japanese Patent Laid-Open No. 7-18139, and the structure and the preparation method thereof are well known. The azo group-containing polysiloxane compound having a structure in which 4,4′-azobis(4-cyanovaleric acid) is bonded to the polydimethylsiloxane chain through an amide bond is commercially available from Wako Pure Chemical Industries, Ltd. under a trade name of VPS-series.

Examples of the epoxy group-containing ethylenically unsaturated monomer include glycidyl (meth)acrylate, β-methylglycidyl (meth)acrylate, 3,4-epoxycyclohexanyl (meth)acrylate and 4-hydroxybutyl acrylate glycidyl ether. For the purpose of preparing a coating composition exhibiting well-balanced curing characteristics and storage stability, it is preferable to use glycidyl (meth)acrylate.

Examples of the fluoroalkyl group-containing unsaturated monomer that can be used for introducing the fluoroalkyl group-containing acrylic block (a-3) include fluoroalkyl (meth)acrylates such as 2-(perfluorohexyl)ethyl (meth)acrylate, 3-perfluorohexyl-2-hydroxypropyl (meth)acrylate, 2-(perfluorooctyl)ethyl (meth)acrylate, 2-(perfluorodecyl)ethyl (meth)acrylate, 2-(perfluoro-3-methylbutyl)ethyl (meth)acrylate, 2,2,2-trifluoroethyl (meth)acrylate, 2,2,3,3-tetrafluoropropyl (meth)acrylate, 1H,1H,5H-octafluoropentyl (meth)acrylate, 2-(perfluorobutyl)ethyl (meth)acrylate and 2,2,3,3,3-pentafluoropropyl (meth)acrylate.

Examples of the other radical polymerizable monomer usable for the preparation of the active energy ray-curable silicone-acrylic copolymer include: styrene and substituted derivatives of styrene in which α-, o-, m-, p-positions are substituted with alkyl, alkoxy, halogen, haloalkyl, nitro, cyano, amide or ester; olefins such as butadiene, isoprene and neoprene; methacrylic or acrylic acid esters of methyl, ethyl, n-propyl, i-propyl, n-butyl, sec-butyl, tert-butyl, pentyl, neopentyl, isoamylhexyl, cyclohexyl, adamantyl, allyl, propargyl, phenyl, naphthyl, anthracenyl, anthraquinonyl, piperonyl, salicyl, cyclohexyl, benzyl, phenethyl, cresyl, triphenylmethyl, dicyclopentanyl and cumyl; and anthranyl amide, acrylonitrile, acrolein, methacrylonitrile, vinyl chloride, vinylidene chloride, vinyl fluoride, vinylidene fluoride, vinylpyridine and vinyl acetate. These compounds may be used each alone, or in combinations of two or more thereof.

Preferable examples of the other radical polymerizable monomer may include monomers having an alicyclic hydrocarbon group such as cyclohexyl (meth)acrylate. By using such a polymerizable monomer, the active energy ray-curable silicone-acrylic copolymer included in the composition for hard coat is made to incorporate therein the other acrylic block (a-4) having a pendant group having an alicyclic hydrocarbon group. Thus, it is possible to provide a copolymer capable of imparting to the hard coat layer a satisfactory adhesion to the substrate.

In the above-described one example of the preparation method, first the azo group-containing polysiloxane compound, acrylic acid and/or methacrylic acid, and the fluoroalkyl group-containing unsaturated monomer, and where necessary, the other radical polymerizable monomers are polymerized. Examples of the polymerization method of these compounds and monomers include bulk polymerization and solution polymerization. In these polymerizations, as described above, the azo group-containing polysiloxane compound functions as the polymerization initiator, and also serves as the source for supplying the radical species having the polysiloxane block. On the other hand, in polymerization, another polymerization initiator may also be used in combination. As the polymerization initiator usable in combination, there can be used compounds generally known as radical polymerization initiators, and examples of such compounds include: azo compounds such as 2,2′-azobisisobutyronitrile, 2,2′-azobis-(2,4-dimethylvaleronitrile), and 2,2′-azobis-(4-methoxy-2,4-dimethylvaleronitrile); organic peroxides such as benzoyl peroxide, lauroyl peroxide, t-butyl peroxypivalate, 1,1′-bis-(t-butyl peroxy)cyclohexane and t-butyl peroxy-2-ethylhexanoate; and hydrogen peroxide. When peroxide is used as the radical polymerization initiator, the peroxide may be used together with a reducing agent as a redox initiator.

The polymerization may be conducted, for example, by stirring for 3 to 48 hours at 60 to 150° C. In the solution polymerization method, the solvent used are not particularly limited; examples of such a solvent include: ethers such as tetrahydrofuran and dioxane; hydrocarbon solvents such as petroleum ether, n-hexane, cyclohexane, toluene and xylene; esters such as ethyl acetate and butyl acetate; alcohols such as methanol, ethanol, isopropanol and butanol; ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone and cyclohexanone; and acetonitrile, N,N-dimethyl formamide and dimethyl sulfoxide. The above-listed solvents can be used each alone or as mixtures of two or more thereof.

Subsequently, the obtained copolymer and the epoxy group-containing ethylenically unsaturated monomer are reacted with each other. In this reaction, the carboxylic acid contained in the acrylic block of the copolymer and the epoxy group contained in (meth)acrylic monomer react with each other, and thus the pendant group having an active energy ray-curable double bond group is introduced into the acrylic block, so as to allow the copolymer to have the active energy ray-curable double bond group-containing acrylic block (a-2). In this way, the active energy ray-curable silicone-acrylic copolymer (A) can be obtained. This reaction may be conducted, for example, by using a glass flask and stirring for 3 to 48 hours at 60 to 150° C.

The parts by weight of the individual components used in this preparation method are as follows: the azo group-containing polysiloxane compound: preferably 0.1 to 40 parts by weight and more preferably 10 to 40 parts by weight; acrylic acid and/or methacrylic acid: preferably 0.2 to 94.8 parts by weight and more preferably 15 to 70 parts by weight; the fluoroalkyl group-containing unsaturated monomer: preferably 4.9 to 49.9 parts by weight and more preferably 5 to 35 parts by weight; and the epoxy group-containing ethylenically unsaturated monomer: preferably 0.2 to 94.8 parts by weight and more preferably 5 to 70 parts by weight. Additionally, when the other radical polymerizable monomer is used, it is preferably used in 0.1 to 45.1 parts by weight and more preferably 0.1 to 35 parts by weight.

On the other hand, in the above-described another example of the preparation method, first the azo group-containing polysiloxane compound, the epoxy group-containing ethylenically unsaturated monomer and the fluoroalkyl group-containing unsaturated monomer, and where necessary, the other radical polymerizable monomers are polymerized. Subsequently, the obtained copolymer and acrylic acid and/or methacrylic acid are reacted with each other, and thus the epoxy group contained in the copolymer is reacted with the carboxyl groups contained in acrylic acid and/or methacrylic acid to yield the active energy ray-curable silicone-acrylic copolymer (A). In this method, the reaction methods such as the polymerization method are the same as described above.

The parts by weight of the individual components used in this preparation method are as follows: the azo group-containing polysiloxane compound: preferably 0.1 to 40 parts by weight and more preferably 10 to 40 parts by weight; the epoxy group-containing ethylenically unsaturated monomer: preferably 5 to 94.8 parts by weight and more preferably 15 to 70 parts by weight; the fluoroalkyl group-containing unsaturated monomer: preferably 4.9 to 49.9 parts by weight and more preferably 5 to 35 parts by weight; and acrylic acid and/or methacrylic acid: preferably 0.2 to 94.8 parts by weight and more preferably 5 to 70 parts by weight. Additionally, when the other radical polymerizable monomer is used, it is preferably used in 0.1 to 45.1 parts by weight and more preferably 0.1 to 35 parts by weight.

By applying these preparation methods, the active energy ray-curable silicone-acrylic copolymer (A) can be prepared in a preferable manner. The active energy ray-curable silicone-acrylic copolymer (A) is used in an amount of preferably about 0.1 to 15% by weight (solid content weight ratio) with respect to the weight of the solid content of the composition for hard coat. When the amount of the active energy ray-curable silicone-acrylic copolymer (A) is less than 0.1% by weight, there occurs a possibility that neither satisfactory water repellency nor satisfactory oil repellency is attained.

Active Energy Ray-Curable Polyfunctional Compound (B)

The composition for hard coat used in the present invention includes the active energy ray-curable polyfunctional compound (B). The inclusion of the active energy ray-curable polyfunctional compound (B) improves the active energy ray curing characteristics of the composition for hard coat, and also enhances the mechanical strength of the obtained hard coat layer. The active energy ray-curable polyfunctional compound (B) has two or more active energy ray-curable groups in one molecule. As the active energy ray-curable polyfunctional compound (B), a compound having in one molecule two or more (meth)acryloyl groups can be used. As the active energy ray-curable polyfunctional compound (B), a compound having three or more (meth)acryloyl groups is preferable. The active energy ray-curable polyfunctional compound (B) may be either a monomer or an oligomer as long as the monomer or the oligomer is a compound having two or more (meth)acryloyl groups.

Examples of such a monomer include: alkylene glycol di(meth)acrylates such as ethylene glycol di(meth)acrylate and propylene glycol di(meth)acrylate; low-molecular-weight polyalkylene glycol di(meth)acrylates such as diethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, dipropylene glycol di(meth)acrylate and tripropylene glycol di(meth)acrylate, and the alkyleneoxide modified compounds thereof; polyol poly(meth)acrylates such as trimethylol propane tri(meth)acrylate, pentaerythritol di-, tri- or tetra(meth)acrylate, ditrimethylol propane tetra(meth)acrylate, dipentaerythritol penta- or hexa(meth)acrylate, and the alkyleneoxide modified compounds thereof; and isocyanuric acid alkylene oxide modified di- or tri(meth)acrylates.

Examples of the oligomer include oligomers of urethane (meth)acrylate, polyester (meth)acrylate, epoxy (meth)acrylate and polyether (meth)acrylate. Among these, urethane (meth)acrylate oligomer is preferably used.

Examples of the urethane (meth)acrylate oligomer include a reaction product obtained by further reacting a hydroxyl group-containing (meth)acrylate with a reaction product between polyol and an organic polyisocyanate. Here, examples of the polyol include: low-molecular-weight polyols such as ethylene glycol, propylene glycol, cyclohexane dimethanol and 3-methyl-1,5-pentanediol; polyether polyols such as polyethylene glycol and polypropylene glycol; and polyester polyols as the reaction products between the above-listed low-molecular-weight polyols and/or polyether polyols, and the acid components such as dibasic acids such as adipic acid, succinic acid, phthalic acid, hexahydrophthalic acid and terephthalic acid or the anhydrides thereof. Preferably used as the organic polyisocyanate are diisocyanates and polyfunctional isocyanates obtained by polymerizing these diisocyanates. Examples of the hydroxyl group-containing (meth)acrylate include 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, pentaerythritol triacrylate and dipentaerythritol pentaacrylate; in particular, preferably used are polyfunctional acrylate compounds such as pentaerythritol triacrylate and dipentaerythritol pentaacrylate. The urethane (meth)acrylate oligomer usable as the active energy ray-curable polyfunctional compound (B) has a number average molecular weight of preferably 300 to 5,000, and more preferably 500 to 3,000. When the molecular weight is less than 300, the volatility is developed so as to be unfavorable for environmental health. When the molecular weight is larger than 5,000, there occurs a possibility that a high viscosity is attained to disturb the handling.

These active energy ray-curable polyfunctional compounds (B) may be used each alone or in combinations of two or more thereof.

As the active energy ray-curable polyfunctional compound (B), a monomer having three or more photopolymerizable groups in one molecule is preferably used. The use of such a monomer enables to enhance the mechanical strength of the obtained hard coat layer. Preferable examples of the active energy ray-curable polyfunctional compound (B) include pentaerythritol triacrylate, trimethylol propane EO-modified triacrylate, dipentaerythritol pentaacrylate and dipentaerythritol hexaacrylate.

The active energy ray-curable polyfunctional compound (B) is used in an amount of preferably about 20 to 99.9% by weight (solid content weight ratio) with respect to the weight of the solid content of the composition for hard coat. When the amount of the photopolymerizable polyfunctional compound (B) is less than 20% by weight, there occurs a possibility that the physical strengths such as the scratch resistance and abrasion resistance are poor.

Photopolymerization Initiator (C)

The composition for hard coat used in the present invention may optionally include the photopolymerization initiator (C). The presence of the photopolymerization initiator (C) enables to promote the polymerization at the time of light irradiation of the active energy ray-curable silicone-acrylic copolymer and the active energy ray-curable polyfunctional compound. Examples of the photopolymerization initiator (C) include alkyl phenone photopolymerization initiators, acyl phosphine oxide photopolymerization initiators, titanocene photopolymerization initiators and oxime ester photopolymerization initiators. Examples of the alkyl phenone photopolymerization initiator include: 2,2-dimethoxy-1,2-diphenylethan-1-one, 1-hydroxy-cyclohexyl-phenyl-ketone, 2-hydroxy-2-methyl-1-phenyl-propan-1-one, 1-[4-(2-hydroxyethoxy)-phenyl]-2-hydroxy-2-methyl-1-propan-1-one, 2-hydroxy-1-[4-[4-(2-hydroxy-2-methyl-propionyl)-benzyl]phenyl]-2-methyl-propan-1-one, 2-methyl-1-(4-methylthiophenyl)-2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1 and 2-(dimethylamino)-2-[(4-methylphenyl)methyl]-1-[4-(4-morpholinyl)phenyl]-1-butanone. Examples of the acyl phosphine oxide photopolymerization initiators include 2,4-6-trimethylbenzoyl-diphenyl-phosphine oxide and bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide. Examples of the titanocene photopolymerization initiator include bis(η5-2,4-cyclopentadien-1-yl)-bis(2,6-difluoro-3-(1H-pyrrol-1-yl)-phenyl)titanium. Examples of the oxime ester photopolymerization initiator include 1,2-octanedione 1-[4-(phenylthio)-2-(O-benzoyloxime)], ethanone 1-[9-ethyl-6-(2-methylbenzoyl) -9H-carbazol-3-yl-1-(O-acetyl oxime), oxyphenyl acetic acid, 2-[2-oxo-2-phenylacetoxyethoxy]ethyl ester, and 2-[2-hydroxyethoxy]ethyl ester. These photopolymerization initiators may be used each alone or in combinations of two or more thereof.

Among the above-listed photopolymerization initiators (C), more preferably used are 2-hydroxy-2-methyl-1-phenyl-propan-1-one, 1-hydroxy-cyclohexyl-phenyl-ketone, 2-methyl-1-(4-methylthiophenyl)-2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1 and 2,12-dimethoxy-1,2-diphenylethan-1-one.

The photopolymerization initiator (C) is used in an amount of preferably about 0 to 15% by weight (solid content weight ratio) with respect to the weight of the solid content of the composition for hard coat. When the amount of the photopolymerization initiator (C) falls outside the above-described range, there occurs a possibility that the physical strength is degraded.

Inorganic Filler (D)

The composition for hard coat used in the present invention may include, where necessary, the inorganic filler (D). The inclusion of the inorganic filler enables to further improve the abrasion resistance of the obtained hard coat layer. It is preferable to use as the inorganic filler (D) an active energy ray-reactive inorganic filler. Active energy ray-reactive silica particles are preferably used as such an active energy ray-reactive inorganic filler. The use of active energy-reactive silica particles enables to satisfactorily fix the silica particles to the resin component when the composition for hard coat is cured by irradiation of active energy ray, and accordingly enables to further enhance the abrasion resistance of the obtained hard coat layer. The active energy ray-reactive silica particle can be prepared by hydrolysis reaction of a polymerizable unsaturated group modified hydrolyzable silane and a silica particle.

As an example of the preparation of such an active energy ray-reactive inorganic filler, Japanese Patent Laid-Open No. 57-131214 proposes an acrylate composition including a colloidal silica treated with a silane coupling agent, as is well known in the art. The use, as an inorganic filler, of such an active energy ray-reactive silica particle enables to further enhance the abrasion resistance of the hard coat layer.

Specific examples of the colloidal silica usable in preparation of the active energy ray-reactive inorganic filler may include the commercial products available from E. I. du pont de Nemours & Co. (USA) under the trade names of Ludox AM, Ludox AS, Ludox LS, Ludox HS and the like, from Nissan Chemical Industries, Ltd. under the trade names of Snowtex Series and Organosol Series, from Monsant Co. (USA) under the trade names of Syton C-30, Syton-200 and the like, and from Nalco Chem. Co. (USA) under the trade names of Nalcoag 1030, Nalcoag 1060, Nalcoag ID-21-64 and the like.

Specific examples of the silane coupling agent used in the surface treatment of the inorganic filler include: γ-methacryloxypropyl trimethoxysilane, γ-methacryloxypropyl triethoxysilane, γ-methacryloxypropyl methyldimethoxysilane, γ-methacryloxypropyl methyldiethoxysilane, γ-acryloxypropyl trimethoxysilane and γ-acryloxypropyl methyldimethoxysilane. Examples of such silane coupling agents include the commercial products available from Shin-Etsu Chemical Co., Ltd., Dow Corning Toray Co., Ltd., GE Toshiba Silicone Co., Ltd. and others.

The active energy ray-reactive inorganic filler more preferably has an average particle diameter of about 5 to 50 nm. The active energy ray-reactive inorganic filler is preferably used in an amount of about 0 to 60% by weight with respect to the weight of the solid content of the composition for hard coat. When the content of the active energy ray-reactive inorganic filler exceeds 60% by weight, there occurs a possibility that the strength of the obtained hard coat layer is degraded.

The composition for hard coat used in the present invention more preferably includes the above-described individual components in the following amounts:

the active energy ray-curable silicone-acrylic copolymer (A): 0.1 to 15% by weight;

the active energy ray-curable polyfunctional compound (B): 20 to 99.9% by weight;

the photopolymerization initiator (C): 0 to 15% by weight; and

the inorganic filler (D): 0 to 60% by weight,

with the proviso that the percentages by weight of the above-described components are all based on the weights of the solid contents in the composition, and the total weight of the solid contents of the individual components is defined as 100% by weight.

Other Components

The composition for hard coat of the present invention may also include additives where necessary. The inclusion of such additives enables to impart appropriate properties to an information recording medium provided with a hard coat layer. However, such additives are not necessarily needed. Examples of the usable additives include TEGO (trade mark) Rad series (manufactured by Tego Co., Ltd.), 2100, 2200N, 2250, 2500, 2600 and 2700 silicone additives.

When such additives are used, the amount thereof is preferably about 0.01 to 1% by weight with respect to the weight of the solid content of the composition for hard coat.

The composition for hard coat used in the present invention may further include an organic solvent as a diluent where necessary. Specific examples of such an organic solvent include: aromatic solvents such as toluene and xylene; aliphatic solvents such as hexane, heptane, octane and mineral spirit; ketone solvents such as methyl ethyl ketone, acetone, methyl isobutyl ketone and cyclohexanone; ether solvents such as diethyl ether, isopropyl ether, tetrahydrofuran, dioxane, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, propylene glycol monomethyl ether, anisole and phenetole; ester solvents such as ethyl acetate, butyl acetate, isopropyl acetate and ethylene glycol diacetate; amide solvents such as dimethylformamide, diethylformamide, dimethyl sulfoxide and N-methylpyrrolidone; cellosolve solvents such as methyl cellosolve, ethyl cellosolve and butyl cellosolve; alcohol solvents such as methanol, ethanol and propanol; and halogenated solvents such as dichloromethane, dichloroethane and chloroform. These solvents may be used each alone or as mixtures thereof.

The composition for hard coat of the present invention may further include, where necessary, usually used additives such as an antistatic agent, a photopolymerization initiator aid, an organic filler, a polymerization inhibitor, an antioxidant, an ultraviolet absorber, a light stabilizer, an antifoamer, a leveling agent and a pigment.

Composition for Hard Coat

The composition for hard coat used in the present invention includes at least the active energy ray-curable silicone-acrylic copolymer (A) and the active energy ray-curable polyfunctional compound (B), and includes, where necessary, the photopolymerization initiator (C) and the inorganic filler (D). Thus, the use of this composition for hard coat enables to form a multi-layered object having a hard coat layer excellent in scratch resistance and abrasion resistance, and additionally excellent in anti-staining property and anti-staining durability even when the hard coat layer is a single layer.

The composition for hard coat used in the present invention is active energy-ray curable. Therefore, the composition has an advantage of needing no heat polymerization at the time of forming the hard coat layer. For example, among various layers included in the multi-layered object, some layers include low heat-resistant materials such as resin portions. The composition for hard coat used in the present invention has an advantage of being capable of satisfactorily forming the hard coat layer even for the multi-layered object including such low heat-resistant materials.

In the preparation method of the composition for hard coat used in the present invention, for example, the composition for hard coat of the present invention can be prepared by mixing the active energy ray-curable silicone-acrylic copolymer (A) and the active energy ray-curable polyfunctional compound (B), and where necessary, the photopolymerization initiator (C) and the inorganic filler (D), and further where necessary, additives, an organic solvent and the like.

Provision of the composition for hard coat used in the present invention on the surface of the light transmitting layer enables to obtain the multi-layered object of the present invention. Examples of the article comprising the multi-layered object include information recording media such as CD, DVD, BD and HD-DVD.

Examples of the method for providing the composition for hard coat on the light transmitting layer include coating methods such as a spin coating method, a dip coating method, a gravure coating method, a spray method, a roller method and a brush coating method. Among these coating methods, the spin coating method is preferable from the viewpoint of the easiness and the cost-efficiency of the production method. The hard coat layer is preferably formed so as for the thickness of the obtained hard coat layer to be 0.1 to 20 μm.

The composition for hard coat provided on the surface of the light transmitting layer is successively cured by being exposed to the irradiation of the active energy ray, and thus the hard coat layer is formed. Examples of the active energy ray include ultraviolet ray, electron ray and visible light. When the light transmitting layer is formed by curing an active energy ray-curable resin, the hard coat layer can be formed by applying the composition for hard coat under the condition that the light transmitting layer is uncured or half cured and by simultaneously curing the composition for hard coat and the light transmitting layer. Such a formation method is preferable in the sense that the adhesion of the hard coat layer to the light transmitting layer is improved and the anti-crack property is also improved.

Information Recording Medium

Examples of an article comprising a multi-layered object of the present invention include an information recording medium. The information recording medium of the present invention is characterized by having a hard coat layer obtained from the above-described composition for hard coat. Hereinafter, the structure and the like of the information recording medium are described.

The information recording medium comprising the multi-layered object of the present invention comprises a supporting substrate, and at least a recording layer, a reflective layer and a light transmitting layer formed from a resin composition or the like on the supporting substrate. On at least one surface of a supporting substrate-side surface and a light transmitting layer-side surface of the information recording medium, a hard coat layer obtained from the above-described composition for hard coat is formed. In the information recording medium comprising the multi-layered object of the present invention, the hard coat layer is formed at least on a recording or reproduction laser beam incident-side surface, out of a light transmitting supporting substrate layer-side surface and a light transmitting layer-side surface, the light transmitting supporting substrate layer being as a supporting substrate and the light transmitting layer being as a protective layer. In other words, in the present invention, the composition for hard coat is applied onto and cured on a light transmitting layer as a supporting substrate or a protective layer, and thus the information recording medium comprising a multi-layered object having the light transmitting layer and the hard coat layer is produced.

Information recording media are generally classified into two types, namely, a type in which the recording or reproduction laser beam is incident on the light transmitting layer-side surface as the protective layer and a type in which the recording or reproduction laser beam is incident on the light transmitting supporting substrate layer side as the supporting substrate. First, description is made on the type in which the recording or reproduction laser beam is incident on the light transmitting layer-side surface as the protective layer.

Information Recording Medium in Which the Recording or Reproduction Laser Beam is Incident on the Light Transmitting Layer-Side Surface, the Light Transmitting Layer Being the Protective Layer:

Such an information recording medium will be described referring to the Figures. FIG. 1 is a schematic cross-sectional view showing one example of the structure of an information recording medium. This information recording medium comprises a supporting substrate (20), a recording layer (4) that functions as an information recording layer on the supporting substrate (20), a light-transmitting layer (7) on the recording layer (4), and a hard coat layer (8) on the light-transmitting layer (7). The laser beam for recording or reproducing is incident through the hard coat layer (8) and the light-transmitting layer (7), and onto the recording layer (4). Therefore, the hard coat layer (8) is required to have light transmission properties.

An information recording medium comprising a multi-layered object of the present invention can be applied to all different manner of recording layers. The information recording medium of the present invention can be applied, for example, to rewritable information recording media (phase-change type recording media) obtained from phase-change type recording materials, pit formation type read only information recording media, and rewritable information recording media obtained from magneto-optical recording materials. Normally, a dielectric layer or a reflective layer is provided on at least one side of the recording layer in order to protect the recording layer and provide an optical effect, but this layer has been omitted in FIG. 1.

Next, a phase-change type recording medium will be described, exemplifying a BD-RE (Blu-ray Disc Rewritable). FIG. 2 is a schematic cross-sectional view showing one example of the layer structure of a BD-RE. In FIG. 2, a BD-RE has a supporting substrate (20) having information pits, pregrooves, and other fine scale concavities-convexities formed on one surface thereof. On this surface, the BD-RE has a reflective layer (3), a second dielectric layer (52), a phase-change recording material layer (41), and a first dielectric layer (51) formed in this order, and further a light transmitting layer (7) and a hard coat layer (8) on the first dielectric layer (51). The BD-RE is constituted in such a manner that a laser beam for recording or reproducing is incident through the hard coat layer (8) and the light transmitting layer (7). In this example, an information recording layer is formed of the reflective layer (3), the second dielectric layer (52), the phase-change recording material layer (41), and the first dielectric layer (51).

The supporting substrate (20) preferably has a thickness of 0.4 to 1.3 mm, and has information pits, pregrooves, and other fine scale concavities-convexities formed on the surface on which the recording layer (4) is formed.

As a supporting substrate (20), various plastic materials including polycarbonate resins, acrylic resins such as polymethyl methacrylate (PMMA), and polyolefine resins and the like may be used preferably. Such a supporting substrate (20) may be produced by injection molding. The supporting substrate (20) is not required to be optically transparent, because the BD-RE is constituted in such a manner that a laser light is incident through the light transmitting layer-side.

Optionally, the reflective layer (3) is deposited by a sputtering process on the supporting substrate (20). The reflective layer (3) may be formed using, as a main component, known inorganic materials as materials for reflective layers such as Au, Ag, Al, and alloys of these metals (for example, Al—Pd—Cu alloy). The reflective layer is preferably formed as a thin film with a thickness of 20 to 200 nm.

Subsequently, the second dielectric layer (52), the phase-change recording material layer (41), and the first dielectric layer (51) are deposited in this order by sputtering process on the reflective layer (3), or on the supporting substrate (20) in the case that no reflective layer is provided.

The phase-change recording material layer (41) has a property of changing reversibly by irradiation of laser light between the crystalline state and the amorphous state, and is formed of materials exhibiting different optical properties between the crystalline state and the amorphous state. Such materials is not particularly limited, however, examples of such material include Ge—Sb—Te, In—Sb—Te, Sn—Se—Te, Ge—Te—Sn, In—Se—Tl, In—Sb—Te, and Sb—Te—Ge—In. There is no limitation to the thickness of the phase-change recording material layer (41), which is for example in a range of about 3 to 50 nm.

The second dielectric layers (52) and the first dielectric layer (51) are formed on the top and under surfaces of the phase-change recording material layer (41), respectively, so as to sandwich the same. The second dielectric layers (52) and the first dielectric layer (51) have not only a function of protecting the phase-change recording material layer (41) mechanically and chemically but also a function as an interference layer for adjusting the optical properties. The second dielectric layers (52) and the first dielectric layer (51) may each consist of either a single layer or a plurality of layers.

Each of the second dielectric layers (52) and the first dielectric layer (51) is preferably formed of an oxide, a nitride, a sulfide, or a fluoride or a composite thereof, containing at least one metal selected from Si, Zn, Al, Ta, Ti, Co, Zr, Pb, Ag, Zn, Sn, Ca, Ce, V, Cu, Fe, and Mg.

There is no limitation to the thickness of the second dielectric layer (52). The thickness of the second dielectric layer (52) is preferably, for example, in a range of about 20 to 150 nm. There is no limitation to the thickness of the first dielectric layer (51). The thickness of the first dielectric layer (51) is preferably, for example, in a range of about 20 to 200 nm. Setting the thicknesses of the second dielectric layers (52) and the first dielectric layer (51) in these ranges makes it possible to adjust reflection.

The light transmitting layer (7) is formed on the above-described first dielectric layer (51). The light transmitting layer (7) is formed by using active energy ray-curable material, for example by means of a spin coating method, or by adhesion of light-transmitting sheet such as a polycarbonate sheet.

The active energy ray-curable material used for the light transmitting layer (7) should be optically transparent, exhibit low optical absorption or reflection in the laser wavelength range to be used, and have low birefringence, and is selected from ultraviolet ray-curable materials and electron ray-curable materials.

The active energy ray-curable material is preferably composed of an ultraviolet ray (electron ray)-curable compound or a composition for polymerizing thereof. Specific examples of the active energy ray-curable material may include the below-listed monomers, oligomer and polymers, containing in the molecules thereof or containing as introduced into the molecules thereof, groups capable of cross-linking or polymerizing under active energy ray irradiation: acrylic acid; methacrylic acid, (meth)acrylic acid ester compounds; acrylic specific monomers; (meth)acrylic double bond-containing monomers such as epoxy (meth)acrylate and urethane (meth)acrylate, and oligomers and polymers thereof; allyl double bond-containing monomers such as diallyl phthalate, and oligomers and polymers thereof; maleic acid derivatives; and the derivatives of these monomers, oligomers and polymers. These active energy ray-curable materials may be used each alone or in combinations of two or more thereof. It is preferable for the active energy ray-curable material to include the urethane (meth)acrylate oligomer, from the viewpoints of the control of the modulus of elasticity and the Tg of the coating film, and the stability with time of the coating film.

The light transmitting layer (7) can be formed, for example, by applying the active energy ray-curable material onto the first dielectric layer (51). In this case, it is preferable to apply the active energy ray-curable material by means of a spin coating method. Thus, the active energy ray-curable material is applied, thereafter cured by irradiation of active energy ray such as ultraviolet ray, and thus the light transmitting layer (7) is formed. The cure degree of the light transmitting layer (7) is preferably a half-cured state from the viewpoints of the adhesion to the hard coat layer (8) to be provided thereon and the anti-crack property. The thickness of the light transmitting layer (7) is preferably 30 to 150 μm and more preferably 50 to 120 μm.

As another example of the light transmitting layer (7) formation, the light transmitting layer can also be formed by using a light transmitting resin sheet. In this case, the active energy ray-curable material usable for forming the above-described light transmitting layer is applied onto the first dielectric layer (51) to form an uncured resin material layer. Successively, on the obtained uncured resin material layer, the light transmitting sheet as the light transmitting layer (7) is placed, thereafter the resin material layer is cured by irradiating active energy ray such as ultraviolet ray, and thus the light transmitting sheet is adhered to be the light transmitting layer (7). As the active energy ray-curable material used for forming the resin material layer, preferable is a material having a viscosity of 3 to 500 cp (25° C.). The formation of the resin material layer can be conducted by means of the spin coating method. The thickness of the resin material layer is, for example, recommended to be about 1 to 50 μm after curing.

As the light transmitting sheet, for example, a polycarbonate sheet having a thickness of 20 to 140 μm is used. More specifically, in the formation of the light transmitting layer (7), a polycarbonate sheet having a predetermined thickness is placed on the uncured resin material layer under a vacuum (0.1 atm or less), then the atmosphere is brought back to the air atmosphere, the resin material layer is cured by irradiating ultraviolet ray, and thus the light transmitting layer (7) can be formed.

On the obtained light transmitting layer (7), the hard coat layer (8) is formed by using the composition for hard coat. In the formation of the hard coat layer, the composition for hard coat is applied onto the light transmitting layer (7) to form the uncured hard coat layer, thereafter the uncured layer is cured by irradiating active energy ray such as ultraviolet ray, electron ray or visible light, and thus the hard coat layer (8) is formed.

The coating method of the composition for hard coat is not particularly limited, and various coating methods such as a spin coating method, a dip coating method and a gravure coating method can be used; however, preferable is the spin coating method that is easy and attains low cost. When a light transmitting sheet is used for formation of the light transmitting layer (7), the hard coat layer can also be formed by means of a method in which the hard coat layer (8) is beforehand formed on a continuous transmitting sheet web by a method such as a gravure coating method, then the light transmitting sheet web is blanked into the information recording medium shape, thereafter the thus obtained piece of the light transmitting sheet is placed on the uncured resin material layer, as described above, and then the curing is conducted.

When the composition for hard coat contains the non-reactive organic diluent, the composition for hard coat is applied to form an uncured hard coat layer, which is then dried by heating to remove the non-reactive organic solvent. Subsequently, the active energy rays may be irradiated to cure the uncured layer and to thereby form the hard coat layer (8). The heating/drying process is preferably carried out at a temperature of for example 40° C. or more and 100° C. or less, and over a time period of for example 30 seconds or more and 8 minutes or less, preferably 1 minute or more and 5 minutes or less, and more preferably 3 minutes or more and 5 minutes or less.

The active energy rays used for curing the composition for hard coat may be properly selected from ultraviolet ray, electron ray, visible light, and other proper active energy ray. Preferably, ultraviolet rays or electron rays are used. The thickness of the hard coat (8) after curing is preferably adjusted to about 0.5 to 5μm.

In this manner, a phase-change type information recording medium such as that shown in FIG. 2 may be produced, which represents an example of an information recording medium in which the recording or reproduction laser beam is incident on the light transmitting layer-side surface.

Information Recording Medium in Which the Recording or Reproduction Laser Beam is Incident on the Light Transmitting Supporting Substrate Layer-Side Surface, the Light Transmitting Supporting Substrate Layer Being the Supporting Substrate:

Next, description is made on the information recording medium in which the supporting substrate-side surface acts as the surface upon which the recording/reproducing beam is incident.

FIG. 3 is a schematic cross-sectional view illustrating another example of the structure of an information recording medium comprising a multi-layered object of the present invention. The information recording medium shown in FIG. 3 comprises a light transmitting supporting substrate layer (22), a recording layer (4) as an information recording layer on one surface of the light transmitting supporting substrate layer (22) which is a light transmitting layer, and a protective layer (6) on the recording layer (4), whereas a hard coat layer (8) is formed on the other surface of the light transmitting supporting substrate layer (22). The hard coat layer (8)-side surface acts as the surface upon which the recording/reproducing beam is incident, and the laser beam for recording or reproducing is incident through the hard coat layer (8) and a light transmitting supporting substrate layer (22), and onto the recording layer (4). Therefore, the hard coat layer (8) is required to have light transmission properties.

FIG. 4 is a schematic cross-sectional view illustrating the structure of an information recording medium (DVD-R) that is another example of the present invention. The information recording medium shown in FIG. 4 comprises a light transmitting supporting substrate layer (22), an organic dye layer (42) on one surface of the light transmitting supporting substrate layer (22), a reflective layer (3) on the organic dye layer (42), and a supporting layer (21) that is bonded to the reflective layer (3) via a protective and adhesive layer (61), whereas a hard coat layer (8) is formed on the other surface of the light transmitting supporting substrate layer (22). The hard coat layer (8)-side surface acts as the surface upon which the recording/reproducing beam is incident.

In addition to the write-once DVD-R disc shown in FIG. 4, a variety of other disc formats, including read-only DVD-ROM, and rewritable formats such as DVD-RAM and DVD-RW and the like can be commercially available. Read-only DVD formats include DVD-video and DVD-ROM, and with these types of information recording media, concavities-convexities known as pits, which are used to record the information signals, are formed in the surface of the light transmitting supporting substrate during production of the substrate, and a metal reflective layer such as A1, and then a protective layer, are formed sequentially on the supporting substrate surface. A supporting layer is then bonded to the protective layer via an adhesive layer, thus completing the information recording medium. In the case of rewritable DVD formats, the information recording layer can be formed in the same manner as for the phase-change type recording medium described above.

In the information recording media shown in FIG. 3 and FIG. 4 in which the recording or reproduction laser beam is incident on the supporting substrate-side surface, the substrate having light transmission properties is used for the light transmitting supporting substrate layer (22). The light transmitting supporting substrate layer (22) is formed, for example, by injection molding of a polycarbonate resin, with information formed in the surface of the resin as a series of prepits or pregrooves. However, materials other than a polycarbonate resin may also be used, and resins such as polyolefin resins can also be employed. The light transmitting supporting substrate layer (22) preferably has a thickness of 0.3 to 1.2 mm, and more preferably 0.4 to 0.8 mm.

The organic dye layer (42) is formed on one side of the obtained light transmitting supporting substrate layer (22). The organic dye layer (42) having an intended layer thickness can be formed as follows: the organic dye is dissolved in a solvent, and the dye solution obtained is applied on the one side by means of the spin coating method and dried. As the organic dye, various cyanine dyes, azo dyes, phthalocyanine dyes and the like can be used.

When the spin coating method is used for the formation of the organic dye layer (42), the organic dye is dissolved in a solvent and is used as an organic dye solution. The solvent is not particularly limited as long as the solvent can sufficiently dissolve the organic dye and does not adversely affect the supporting substrate. The concentration of the organic dye is preferably about 0.01 to 10% by weight.

The layer thickness of the organic dye layer (42) is appropriately selected according to the used dye. The layer thickness of the organic dye layer is preferably about 10 to 300 nm and particularly preferably about 60 to 250 nm.

On the obtained organic dye layer (42), the reflective layer (3) is provided by means of the sputtering method. As the material for the reflective layer, there is used a material which is sufficiently high in reflectance in the wave range of the reproduction light. As such a material, the elements such as Au, Ag and Al are used as the main components.

There are no particular restrictions on the thickness of the reflective layer, although values from about 10 to 300 nm are preferred, and values from about 80 to 200 nm are particularly desirable.

A supporting layer (21) is usually bonded to the reflective layer (3) via a protective and adhesive layer (61). This supporting layer (21) can use the same material as that used for the light transmitting supporting substrate layer (22) The layer thickness of the supporting layer (21) is preferably about 0.3 to 1.2 mm and more preferably about 0.4 to 0.8 mm.

There are no particular restrictions on the material used for the protective and adhesive layer (61), provided it is capable of bonding the supporting layer (21) and the light transmitting supporting substrate layer (22), and protecting the reflective layer from external forces, and conventional organic or inorganic materials can be used.

The hard coat layer (8) is formed by using the composition for hard coat on the other surface of the light transmitting supporting substrate layer (22). As described above, the light transmitting supporting substrate layer (22) corresponds to the light transmitting layer of the present invention.

The obtained information recording medium is the medium in which hard coat layer (8)-side acts as the surface upon which the recording/reproducing beam is incident. The recording/reproducing beam uses a laser beam with a wavelength of 650 or 660 nm, blue laser beam and the like.

In the manner described above, an information recording medium in which the supporting substrate-side surface acts as the surface upon which the recording/reproducing beam is incident may be produced.

EXAMPLES

The present invention is described more specifically with reference to following Examples, but is not limited to these Examples. In following Examples, “part(s)” and “percentage” are given in terms of weight unless otherwise indicated.

Production Example 1 Production of an Active Energy Ray-Curable Silicone-Acrylic Copolymer (1) Liquid

A mixture was prepared by mixing 227 g (a quantity for the solid content weight ratio of the polysiloxane chain in the active energy ray-curable silicone-acrylic copolymer to be 25% by weight) of VPS-1001 (an azo group-containing polysiloxane compound, manufactured by Wako Pure Chemical Industries, Ltd., molecular weight of the polysiloxane chain: 10,000, solid content: 27%) with a monomer mixture (the content of a fluorine-containing unsaturated monomer in the active energy ray-curable silicone-acrylic copolymer: 30% by weight) composed of 74 g of acryl ester 17FE (manufactured by Mitsubishi Rayon Co., Ltd.) and 37 g of acrylic acid. In a 1000 ml glass vessel equipped with stirring blades, a nitrogen introduction tube, a cooling tube and a dropping funnel, the obtained mixture was dropped at a constant rate, under nitrogen atmosphere, to 310 g of propylene glycol monomethyl ether acetate heated to 100° C. over a period of 3 hours, and thereafter, the resultant was allowed to react at 100° C. for 30 minutes.

Thereafter, to the obtained reaction liquid, 13 g of a liquid of propylene glycol monomethyl ether acetate containing 0.5 g of t-butylperoxy-2-ethylhexanoate was dropped at a constant rate over a period of 30 minutes, and the obtained reaction liquid was further allowed to react at 100° C. for 1.5 hours.

To this reaction liquid, under air bubbling, a mixture composed of 74 g of glycidyl methacrylate and 98 g of propylene glycol monomethyl ether acetate was dropped over a period of 1 hour, and then the obtained reaction liquid was further allowed to react over a period of 8 hours to yield the active energy ray-curable silicone-acrylic copolymer (1).

Production Example 2 Production of an Active Energy Ray-Curable Silicone-Acrylic Block Copolymer (2) Liquid

A mixture was prepared by mixing 227 g (a quantity for the solid content weight ratio of the polysiloxane chain in the active energy ray-curable silicone-acrylic copolymer to be 25% by weight) of VPS-1001 (an azo group-containing polysiloxane compound, manufactured by Wako Pure Chemical Industries, Ltd., molecular weight of the polysiloxane chain: 10,000, solid content: 27%) with a monomer mixture (the content of a fluorine-containing unsaturated monomer in the active energy ray-curable silicone-acrylic copolymer: 30% by weight) composed of 74 g of acryl ester 17FE (manufactured by Mitsubishi Rayon Co., Ltd.), 74 g of cyclohexyl methacrylate and 15 g of acrylic acid. In a 1000 ml glass vessel equipped with stirring blades, a nitrogen introduction tube, a cooling tube and a dropping funnel, the obtained mixture was dropped at a constant rate, under nitrogen atmosphere, to 310 g of propylene glycol monomethyl ether acetate heated to 100° C. over a period of 3 hours, and thereafter, the resultant was allowed to react at 100° C. for 30 minutes.

Thereafter, to the obtained reaction liquid, 13 g of a solution of propylene glycol monomethyl ether acetate containing 0.5 g of t-butylperoxy-2-ethylhexanoate was dropped at a constant rate over a period of 30 minutes, and the obtained reaction liquid was further allowed to react at 100° C. for 1.5 hours.

To this reaction liquid, under air bubbling, a mixture composed of 22 g of glycidyl methacrylate and 98 g of propylene glycol monomethyl ether acetate was dropped over a period of 1 hour, and then the obtained reaction liquid was further allowed to react over a period of 8 hours to yield the active energy ray-curable silicone-acrylic copolymer (2).

Production Example 3 Preparation of the Dispersion of the Active Energy Ray-Reactive Inorganic Filler

A mixture composed of 165 parts by weight of isopropanol, 106 parts by weight of IPA-ST (30% colloidal silica dispersion, manufactured by Nissan Chemical Industries, Ltd.), 8.1 parts by weight of γ-methacryloxypropyl trimethoxysilane (trade name: KBM-503, manufactured by Shin-Etsu Chemical Co., Ltd.) and 1.0 part by weight of distilled water was stirred for 3 hours under heating at 80° C. Then, 165 parts by weight of propylene glycol monomethyl ether was added to the mixture, and subsequently, isopropanol and water were distilled off under reduced pressure to yield a slightly clouded liquid containing the active energy ray-reactive inorganic filler.

Preparation of a Composition for Hard Coat

The active energy ray-curable silicone-acrylic copolymer (1) and (2) obtained in above-described Production Examples were used respectively, and according to the composition shown in Table 2, the individual ingredients were mixed together to prepare each compositions for hard coat.

Example 1 Production of an Information Recording Medium

An information recording medium having a layer structure shown in FIG. 2 was produced in the following manner. Using a disc shaped supporting substrate (20) (formed from polycarbonate, diameter 120 mm, thickness 1.1 mm) in which information recording grooves had been formed, sputtering was used to form a reflective layer (3) of thickness 100 nm comprising Al₉₈Pd₁Cu₁ (atomic ratio) on the groove-side surface of the substrate. The depth of the grooves, which is represented by light-path length at a wavelength γ=405 nm, was set into γ/6. The recording track pitch in the groove-recording scheme was set into 0.32 μm.

Subsequently, sputtering with an Al₂O₃ target was used to form a second dielectric layer (52) of thickness 20 nm on the surface of the reflective layer (3). Sputtering using an alloy target comprising a phase-changing material was then used to form a recording layer (4) of thickness 12 nm on the surface of the second dielectric layer (52). The composition (atomic ratio) of the recording layer (4) was Sb₇₄Te₁₈(Ge₇In₁). Sputtering with a ZnS (80 mol %)-SiO₂ (20 mol %) target was then used to form a first dielectric layer (51) of thickness 130 nm on the surface of the recording layer (4).

Subsequently, a radical polymerizable, ultraviolet ray-curable material with the composition shown in the following Table 1 was applied onto the surface of the first dielectric layer (51) by spin coating, and was then irradiated with a weak ultraviolet ray of 20 mJ/cm² in integrated light quantity to form a 98 μm thick half-cured light transmitting layer (7).

TABLE 1 Light transmitting layer: Composition of ultraviolet ray-curable material Urethane acrylate oligomer 75 parts by weight (a compound obtained by acrylating the both terminals of polycarbonate diol (molecular weight: 1000, trade name: Nipporan 981, manufactured by Nippon Polyurethane Industry Co., Ltd.) with hydrogenated MDI and 2-hydroxyethyl acrylate) Tetrahydrofurfuryl acrylate 25 parts by weight Photopolymerization initiator  3 parts by weight (1-hydroxycyclohexyl phenyl ketone)

Next, on the obtained half-cured light transmitting layer (7), a composition for hard coat having the composition of Example 1 shown in Table 2 was applied by spin coating to form a coating film. The obtained coating film was dried in a hot air dryer set at 80° C. for 180 seconds, and thereafter irradiated under nitrogen gas flow with electron beam to be cured to form a hard coat layer (8). The irradiation of electron beam was conducted with an electron ray irradiation apparatus Min-EB (manufactured by Ushio Inc.) under the conditions that the electron ray acceleration voltage was 50 kV and the irradiation dose was 100 kGy. The oxygen concentration in the irradiation atmosphere was 80 ppm. The thickness of the hard coat layer (8) after curing was 3 μm. Thereafter, the light transmitting layer was completely cured by irradiating ultraviolet ray with an integrated light quantity of 3 J/cm².

Example 2 Production of an Information Recording Medium

The composition for hard coat of Example 2 shown in Table 2 was applied and dried in the same manner as in Example 1, and then an information recording medium was produced in the same manner as in Example 1 except that the hard coat layer (8) and the light transmitting layer were simultaneously cured by ultraviolet ray irradiation with an integrated light quantity of 3 J/cm² without applying electron beam irradiation for curing.

Example 3 Production of an Information Recording Medium

An information recording medium was produced in the same manner as in Example 1 except that, as a composition for hard coat, the composition for hard coat having the composition of Example 3 shown in Table 2 was used.

Example 4 Production of an Information Recording Medium

An information recording medium was produced in the same manner as in Example 2 except that, as a composition for hard coat, the composition for hard coat having the composition of Example 4 shown in Table 2 was used.

Example 5 Production of an Information Recording Medium

The composition for hard coat of Example 5 shown in Table 2 was directly applied by spin coating to a polycarbonate layer that was a light transmitting supporting substrate layer (22) on the recording/reproduction beam incident-side of a DVD-R disc to form a coating film. The obtained coating film was dried in a hot air dryer set at 80° C. for 180 seconds, and thereafter irradiated with ultraviolet ray at an integrated light quantity of 1 J/cm² to be cured to form a hard coat layer (8), and thus an information recording medium was obtained.

Comparative Examples 1 to 3

According to the compositions of Comparative Examples 1 to 3 shown in Table 3, individual ingredients were mixed together to prepare compositions for hard coat respectively. The obtained compositions for hard coat were used to produce information recording media respectively in the same manner as in Example 2.

The information recording media obtained in Examples and Comparative Examples were used to conduct evaluations as follows.

Evaluation of Appearance

The surface of each of the hard coat layers of the information recording media obtained in Examples and Comparative Examples was visually observed for evaluation. The evaluation results obtained are shown in Tables 2 and 3.

Abrasion Resistance Test

The hard coat layers were produced respectively in the same manner as in Examples 1 to 5 and Comparative Examples 1 to 3 except that no information recording layer is formed. The surface of each of the hard coat layers was subjected to 500-times abrasion operations by applying a load of 500 g with a taper abrasion tester in accordance with JIS K7204:1999. An CS-10F Type IV truck wheel was used. The haze value of the surface of the hard coat layer after 500-times abrasion operations was measured with a haze meter (manufactured by Suga Test Instruments Co., Ltd.), and the difference between the haze value after the abrasion operations and the haze value before the abrasion operation was obtained as ΔHaze. The obtained results are shown in Tables 2 and 3.

Electric Signal Properties

The tracking error signal voltage generated on the basis of the reflected light from an information recording medium received with an optical pickup was compared with a beforehand set reference value to measure the variation values of the tracking error signal voltage, and the variability of these values was obtained as the variation value. The obtained results are shown in Tables 2 and 3. A case with the variation value of 35% or more was evaluated as “not good” and a case with the variation value of less than 35% was evaluated as “good”. The obtained results are shown in Tables 2 and 3.

Evaluation of Anti-Staining Property

A static contact angle was measured with a contact angle meter, Face Contact-Anglemeter manufactured by Kyowa Interface Science Co., Ltd. As measurement liquids, pure water and n-octane were used. The measurement environment was such that the temperature was 20° C. and the relative humidity was 60%. First, in the information recording media, the contact angles before rubbing, which is described later, were measured.

Evaluation of Anti-Staining Durability

Subsequently, the contact angles after rubbing with ethanol were measured. Bencot (manufactured by Asahi Kasei Fibers Corp.) was impregnated with ethanol, and then was pressed against the surface of the hard coat of each of the test samples with a load of 1 kg/cm², and reciprocated 100 times, and the contact angle was measured under the same conditions as described above. The measurement of the contact angles after the rubbing enables to evaluate the anti-staining durability; the smaller is the change of the contact angle between before and after the rubbing, the higher is the anti-staining durability. The obtained results are shown in Tables 2 and 3.

TABLE 2 Example 1 Example 2 Example 3 Example 4 Example 5 Composition Active energy ray-curable (1) 10 10 — — 10 for hard coat silicone-acrylic copolymer (A) (2) — — 10 10 — Active energy ray-curable polyfunctional 90 90 60 60 60 compound (B)*¹ Photopolymerization initiator (C)*² — 8 — 8 8 Reactive inorganic filler (D)*³ — — 30 30 30 Propylene glycol monomethyl ether*⁴ 224 224 224 224 224 Fluorinated additive*⁵ — — — — — Photo-reactive silicone additive*⁶ — — — — — Curing method of composition for hard coat EB UV EB UV UV Degree of cure of light transmitting layer half-cured half-cured half-cured half-cured * at the time of applying composition for hard coat Appearance good good good good good Abrasion resistance test; ΔHaze 26 27 13 12 12 Electric signal properties good good good good good Anti-staining property, and Contact angle before 106 104 107 104 104 Anti-staining durability with pure water rubbing (deg) after 105 102 105 102 102 rubbing Contact angle before 49 47 44 44 47 with n-octane rubbing (deg) after 48 41 41 39 40 rubbing *: In Example 5, a polycarbonate layer was used as the light transmitting layer, and the composition for hard coat was directly applied to this polycarbonate layer.

TABLE 3 Comparative Comparative Comparative example 1 example 2 example 3 Composition Active energy ray-curable (1) — — — for hard coat silicone-acrylic copolymer (A) (2) — — — Active energy ray-curable polyfunctional 100 100 100 compound (B)*¹ Photopolymerization initiator (C)*² 8 8 8 Reactive inorganic filler (D)*³ — — — Propylene glycol monomethyl ether*⁴ 207 207 207 Fluorinated additive*⁵ 3 — — Photo-reactive silicone additive*⁶ — 3 — Curing method of composition for hard coat UV UV UV Degree of cure of light transmitting layer half-cured half-cured half-cured at the time of applying composition for hard coat Appearance clouded clouded good Abrasion resistance test; ΔHaze 33 35 20 Electric signal properties not good not good good Anti-staining property, and Contact angle before rubbing 105 100 60 Anti-staining durability with pure water after rubbing 93 90 50 (deg) Contact angle before rubbing 60 less than 5 less than 5 with n-octane after rubbing 46 less than 5 less than 5 (deg) In the Tables 2 and 3: *¹Dipentaerythritol hexaacrylate *²Irgacure 184, 1-hydroxy-cyclohexyl-phenyl-ketone *³reactive inorganic filler prepared in Production Example 3 (parts by weight in the Tables 2 and 3 represents parts by weight of solid content). *⁴Solvent *⁵Megafac F-484, manufactured by Dainippon Ink Chemical Industries, Co. Ltd. *⁶BYK-3500, manufactured by BYK Chemie Japan Co., Ltd.

As can be seen from the results shown in Table 2, each of the hard coat layers of the present invention is such that: the abrasion resistance is satisfactory; the water contact angle is high both before and after the rubbing, and the water repellency and the water repellency durability are excellent; further, a high n-octane contact angle is attained although no additives such as a silicone additive and a fluorinated additive are added, and the n-octane contact angle is high both before and after the rubbing; the oil repellency and the oil repellency durability are excellent.

On the other hand, in Comparative Examples 1 and 2 in which no active energy ray-curable silicone-acrylic copolymer was used, but a commercially available fluorinated compound or an active energy ray-curable silicone additive was added, the abrasion resistance was poor. In these Comparative Examples, although the water contact angle was high, Comparative Example 1 was poor in anti-staining durability and Comparative Example 2 was low in n-octane contact angle. Further, in these Comparative Examples, the surface was clouded and the electric properties of the information recording medium were impaired. In Comparative Example 3 in which no fluorinated compound and no active energy ray-curable silicone additive was included, although the surface was not found to be clouded and the electric properties of the information recording medium were satisfactory, water contact angle and n-octane contact angle were low and accordingly poor in the anti-staining property.

A multi-layered object of the present invention has a single-layered hard coat layer, and hence is provided with anti-staining property, scratch resistance and abrasion resistance, without deteriorating the optical properties and recording properties as required for information recording media and various display elements, further is excellent in the anti-staining durability enabling a long-term maintenance of the anti-staining property. Further, the hard coat layer in the multi-layered object of the present invention is active energy ray-curable, and hence there can be provided inexpensively and easily a multi-layered object that has a hard coat excellent in production efficiency and production cost, and having anti-staining property, anti-staining durability, scratch resistance and abrasion resistance. In particular, when a hard coat layer is formed on the surface of the light transmitting layer of an information recording medium, the recording/reproduction on the information recording medium can be conducted without deteriorating the optical properties and recording properties required for information recording media, and additionally there can be obtained an information recording medium excellent in scratch resistance, abrasion resistance, anti-staining property and anti-staining durability. 

1. A multi-layered object comprising a hard coat layer and a light transmitting layer, wherein the hard coat layer is formed from a composition for hard coat comprising: an active energy ray-curable silicone-acrylic copolymer (A); and an active energy ray-curable polyfunctional compound (B), and wherein the active energy ray-curable silicone-acrylic copolymer (A) contains: a polysiloxane block (a-1) represented by the following formula (I):

wherein R¹s and R²s are the same or different and each represents a hydrogen atom, an alkyl group having 1 to 6 carbon atoms or a nitrile group; R³s are the same or different and each represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms; R⁴s are the same or different and each represents a hydrogen atom, a halogen atom, a substituted or nonsubstituted alkyl group having 1 to 6 carbon atoms or a phenyl group having 6 to 12 carbon atoms; p and q are the same or different and each represents an integer of 0 to 6; and m represents an integer of 0 to 600, an acrylic block (a-2) containing an active energy ray-curable double bond group, and a fluoroalkyl group-containing acrylic block (a-3).
 2. The multi-layered object according to claim 1, wherein the composition for hard coat further comprises a photopolymerization initiator (C).
 3. The multi-layered object according to claim 1, wherein the composition for hard coat further comprises an inorganic filler (D).
 4. The multi-layered object according to claim 1, wherein the active energy ray-curable silicone-acrylic copolymer (A) is composed of: 0.1 to 40% by weight of the polysiloxane block (a-1); 5 to 94.8% by weight of the acrylic block (a-2) containing active energy ray-curable double bond group; and 4.9 to 49.9% by weight of the fluoroalkyl group-containing acrylic block (a-3).
 5. The multi-layered object according to claim 1, wherein the light transmitting layer is formed from an active energy ray-curable material containing a urethane (meth)acrylate oligomer.
 6. An information recording medium comprising the multi-layered object according to claim
 1. 7. A method for producing a multi-layered object comprising a hard coat layer and a light transmitting layer, the method comprising the step of: applying a composition for hard coat onto a light transmitting layer to form a hard coat layer, wherein the composition for hard coat comprises: an active energy ray-curable silicone-acrylic copolymer (A); and an active energy ray-curable polyfunctional compound (B), and wherein the active energy ray-curable silicone-acrylic copolymer (A) contains: a polysiloxane block (a-1) represented by the following formula (I):

wherein R¹s and R²s are the same or different and each represents a hydrogen atom, an alkyl group having 1 to 6 carbon atoms or a nitrile group; R³s are the same or different and each represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms; R⁴s are the same or different and each represents a hydrogen atom, a halogen atom, a substituted or nonsubstituted alkyl group having 1 to 6 carbon atoms or a phenyl group having 6 to 12 carbon atoms; p and q are the same or different and each represents an integer of 0 to 6; and m represents an integer of 0 to 600, an acrylic block (a-2) containing an active energy ray-curable double bond group, and a fluoroalkyl group-containing acrylic block (a-3).
 8. The method for producing the multi-layered object according to claim 7, wherein the hard coat layer is formed by applying the composition for hard coat under the condition that the light transmitting layer is uncured or half cured. 